	title = {Highly improved thermoelectric performance of BiCuTeO achieved by decreasing the oxygen content},
	volume = {15},
	year = {2020},
	note = {n/a},
	month = {2020},
	pages = {100248},
	abstract = {<p>BiCuTeO is a promising thermoelectric material owing to its intrinsically low thermal conductivity and high carrier concentration. This study investigated the influence of stoichiometric oxygen deficiencies on the thermoelectric performance of BiCuTeO. Bulk BiCuTeO1-x (0.16 >= x) samples were prepared by a conventional solid state reaction and pelleted by hot pressing. Synchrotron X-ray diffraction, electron probe X-ray microanalysis, scanning electron microscopy, and transmission electron microscopy characterized the samples. A maximum value of 1.06 was achieved for the dimensionless figure of merit ZT at 673~K for BiCuTeO0.88, which is approximately 49\% better than the current maximal ZT value for BiCuTeO. The power factor was noticeably improved owing to increases in the electrical conductivity and Seebeck coefficient. Moreover, the optimal oxygen deficiency could introduce nanoparticles, resulting in reduced thermal conductivity. The findings will be important for the future development of metal oxide thermoelectric materials for use in practical thermoelectric devices.</p>
},
	keywords = {Electrical conductivity, Figure of merit, Hot pressing, Secondary phases, thermal conductivity},
	isbn = {2542-5293},
	url = {https://www.sciencedirect.com/science/article/pii/S2542529320300729},
	author = {H.-C. Chang and Chen, T.-H. and R. Sankar and Y-J Yang and L.-C. Chen and K.-H. Chen}
}